Formation grouting method and composition useful therefor

ABSTRACT

A method of grouting porous gas--and petroleum--bearing formations with a cementitious material comprising ultrafine ground slag is useful for primary and remedial cementing of a wellbore. A composition is provided which comprises water, a dispersant, slag and an accelerator to activate the slag.

CROSS-REFERENCES TO RELATED APPLICATIONS

This application is a continuation-in-part of pending application Ser. No. 07/278,970 filed on Dec. 2, 1988 now U.S. Pat. No. 5,026,215.

BACKGROUND OF INVENTION

1. Field of the Invention

This invention relates to a method of grouting formations. The method is useful for stabilizing and strengthening soil and rock formations as well as underground structures associated with buildings, tunnels and dams. The invention also relates to a composition suitable for use in the method of the invention. The method and composition of the invention are particularly useful for preventing permeation of water and therefore are especially useful in grouting dam curtains and containing and stabilizing hazardous wastes including nuclear waste material. Also, the method and composition of the invention are particularly useful for grouting porous gas--and petroleum--bearing formations.

2. Description of the Prior Art

The present method utilizes a MICROFINE (ultrafine ground) slag as a component of an economical grouting composition having an excellent combination of properties for the above-mentioned uses. It has earlier been proposed in D. W. Moller, H. L. Minch, J. P. Welsh, "Ultrafine Cement Pressure Grouting to Control Ground Water in Fractured Granite Rock" ACI Proceedings, SP 83-8, Fall Convention, Kansas City, 1983, and in W. J. Clarke, "Performance Characteristics of Microfine Cement", ASCE preprint 84-023, Geotechnical Conference, Atlanta, May 14-18, 1984, (the disclosures of both of these publications being incorporated herein by reference), to use ultrafine ground cement for underground strengthening and water control. The cement proposed for such use was a co-ground combination of slag and portland cement having fineness properties of a specific surface area of 8,880 cm² /g and a grain size of about 50% of particles below about 4 micrometers.

The use of more finely divided slag having a specific surface area greater than 9,500 cm² /g in a composition for sealing, stabilizing and strengthening formations is described in U.S. Pat. No. 4,761,183 granted on Aug. 2, 1988 to the present applicant, the disclosure of which is incorporated herein by reference.

Forss U.S. Pat. No. 4,306,912 issued on Dec. 22, 1981, describes the activation of slag by use of an accelerator comprising sodium hydroxide.

U.S. Pat. No. 4,897,119 granted on Jan. 30, 1990 to the present applicant, (the disclosure of which is incorporated herein by reference), describes dispersants useful for ultrafine ground slag grouting compositions.

"Worldwide Cementing Practices", Dwight K. Smith, 1991, American Petroleum Institute, Johnston Printing Company, Dallas, Tex.; "Well Cementing", Erik, B. Nelson, 1990, Elsevier Science Publishers, Amsterdam; and "Cementing", Dwight K. Smith, 1990, Society of Petroleum Engineers, New York, the disclosure of all three of these publications being incorporated herein by reference, disclose techniques for cementing wells and gas--and oil--bearing formations, especially the use of portland cement for such purposes and cement additives.

SUMMARY OF THE INVENTION

According to the present invention there is provided method of grouting porous gas--and petroleum--bearing formations, which comprises injecting into said formation a composition comprising a particulate slag, said composition comprising:

a. water

b. particulate slag, having a specific surface area greater than about 9,500 cm² /g, with less than 3 wt. percent of the particles of said slag being larger than 7.8 micrometers in diameter; the proportions of water and slag being within a water to slag weight ratio range of between 0.5:1 and 10:1;

c. at least one dispersant in an amount effective to disperse the particles of said particulate slag; and

d. an accelerator in an amount effective to provide hydraulic reactivity to said slag.

Also provided according to the present invention is a grouting composition comprising a particulate slag, said composition comprising:

(a) water;

(b) at least one dispersant in an amount effective to disperse the particles of said particulate slag;

(c) as said particulate slag, a microfine slag having a specific surface area greater than about 9,500 cm² /g, with less than 3 wt. percent of the particles of said slag being larger than 7.8 micrometers in diameter; the proportions of water and slag being within a water to slag weight ratio of between 0.5:1 and 1:1; and

(d) an accelerator in an amount effective to provide hydraulic reactivity to said slag.

Further provided according to the present invention is a grouting composition comprising a particulate slag, said composition comprising:

(a) water;

(b) at least one dispersant in an amount effective to disperse the particles of said particulate slag;

(c) as said particulate slag, a microfine slag having a specific surface area greater than about 9,500 cm² /g, with less than 3 wt. percent of the particles of said slag being larger than 7.8 micrometers in diameter; the proportions of water and slag being within a water to slag weight ratio range of between 0.5:1 and 10:1; and

(d) an accelerator in an amount effective to provide hydraulic reactivity to said slag; said composition having been prepared by mixing in sequence (a) with (b) to form a first mixture, then adding (c) to form a second mixture, then adding (d) to said second mixture, and subjecting the resulting composition to strong agitation.

There is a need to provide a method of grouting formations which achieves high permeation of grout into the formation with a grout which has desired setting, hardening and settlement properties. There is a particular need for such method in well cementing procedures.

Because of the large quantities of grouting composition which must be employed when used to stabilize or strengthen formations or to contain water in such formations, the grouting composition not only must possess the desired combination of properties, but also needs to be economical.

The present invention provides a method of grouting which enables the sealing of a formation such that the formation attains a very low permeability to water and other fluids and thus is useful for such applications as stabilizing and containing hazardous waste. Compositions used in the present invention have an unusual ability to penetrate such formations and have desirable characteristics of setting and hardening time. These compositions also are economical and non-polluting, so that they may be used in containment of hazardous waste without adding to the problem.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a ternary phase diagram showing the relative proportions of calcium, aluminum and silicon oxides in cements, slag and related products.

FIG. 2 schematically illustrates a sectional elevation showing dam curtain grouting.

FIG. 3 schematically illustrates a sectional elevation of foundation grouting.

FIG. 4 schematically illustrates a sectional elevation showing nuclear waste containment.

FIG. 5 schematically illustrates a sectional elevation showing stabilization of hazardous waste.

FIG. 6 is a diagrammatic sectional illustration of tube-a-machette grout injection.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The following Table 1 illustrates examples of the chemical composition of portland cement, M5 slag/cement and M1 slag.

                  TABLE 1                                                          ______________________________________                                                PORTLAND      M5     M1                                                 ______________________________________                                         SiO.sub.2                                                                               22.             30.6   35.4                                           Al.sub.2 O.sub.3                                                                        5.2             12.4   16.                                            Fe.sub.2 O.sub.3                                                                        3.2             1.1    0.3                                            CaO      65.2            48.4   43.3                                           MgO      1.3             5.8    3.5                                            SO.sub.3 1.9             0.8    0.3                                            ______________________________________                                    

As is shown in Table 1 and in the ternary diagram of FIG. 1, portland cement is high in calcium oxide and low in silicon dioxide while M1 slag contains a lower content of calcium oxide and a higher content of silicon dioxide. The composition of M5 slag/cement is between that of portland and M1 slag. In the United States Geochemical Corporation markets ultrafine cement under the trademark MICROFINE, and sells M5 slag/cement under the trademark MC-500 and M1 slag under the trademark MC-100.

The major advantage of MICROFINE cement over portland is the ability to permeate fine sands and finely cracked rock. M1 and M5 permeate fine sands while portland does not permeate coarse sand. This provides the justification for using MICROFINE cement for permeation grouting dam curtains, stabilizing hazardous wastes and containment of nuclear wastes.

Permeation testing has showed that M1 MICROFINE cement permeates fine sand at 3 times the volume of M5. This indicates that particulate grouts with particle size one third the fine sand openings operate like solution grouts where most of the particles pass through the sand.

Low viscosity is required for fast permeation of the MICROFINE cements. This is provided by higher water/cement weight ratios (above 1:1) and the use of dispersants. The viscosity of all water ratios of M1 or of M5 are lower than portland. At 2:1 water to cement ratio the viscosity of M1 and of M5 is 7 and 9 centipoises, respectively. Lower water/cement (WC) ratios (water below 1:1) are usable in coarser formations using higher pressure injection to obtain low formation permeability for hazardous waste containment.

Permeability of neat MICROFINE and portland cements were laboratory tested by taking samples of hazardous waste water and determining the permeability of the neat (no sand content) cement to the waste water. Permeability rates through M1 are very low at 10⁻⁹ cm/sec after 15,000 minutes. M5 gave almost 10⁻⁹ and portland gave lower than 10⁻⁷ cm/sec permeability. These low permeability rates indicate that M1, M5 or M1 plus M3 (MICROFINE portland) MICROFINE cements may be used in well cementing, to contain nuclear wastes and to stabilize hazardous waste plumes.

The grouting composition used in the present invention comprises an ultrafine slag, water in which the slag is dispersed, a dispersant and an accelerator which increases the hydraulic reactivity of the slag.

The ultrafine slag is a cementitious material (CM) having a specific surface area (SSA) greater than 9,500, preferably greater than 11,000 and most preferably greater than 13,000 or 14,000 square centimeters per gram and, by weight, less than 3%, preferably less than 1.5% and most preferably no particles of the slag larger than 7.8 micrometers in diameter. Especially for well cementing applications, it is preferred that the MICROFINE slag has less than 2 wt. percent particles larger than 10 microns in diameter. (The surface area and particle size are measured by the use of the Microtrac® instrument further described hereinbelow.)

An optional cementitious material in the composition is cement having an SSA greater than 6,000 cm² /g, or better, greater than 8,000 cm² /g. Still better such cement has an SSA greater than 10,000, preferably greater than 11,000, with, by weight, less than 16%, preferably less than 7% and most preferably less than 3% of particles of the cement larger than 7.8 micrometers in diameter as measured by the Microtrac® instrument. The preferred optional cement is portland cement. When used, preferably the optional cement has an SSA of at least about 9,000 cm² /g, more preferably 10,000 about cm² /g and is mixed with ultrafine slag having an SSA of at least about 14,000 cm² /g, the mixture having an SSA of at least about 12,000 cm² /g. It is particularly preferred, especially for gas--and petroleum well cementing, with MICROFINE slag, to additionally use portland cement having a particle size wherein less thn 2 wt. percent of the particles of said portland cement are larger than 10 microns in diameter, the slag being at least 40 percent by weight of the total of portland cement and slag.

The hydration of slag differs from that of portland cement in many aspects. The most striking difference is that slag powder is a homogenous material (glass) with a rather uniform reactive surface, while clinker powder is largely inhomogeneous. The clinker powder is composed of small areas of various minerals with highly different solubilities and reactivities. The reaction with water is highly exothermic and the hydrated structure is built up from a needle-like structure. The reaction between slag-glass and water is only slightly exothermic, and the hydrated structure is built up from a rather homogeneous mass. To be able to reach high early strength the particles in a hydrating body containing slag need to be very close. One way this is made possible is by reducing water content in all types of slag-bearing hydrating bodies.

The WC weight ratio in the present invention is from 0.5:1 to 10:1. For low formation permeability in water control and hazardous waste containment a WC ratio of 0.5:1 to 2:1 is employed. For formation strengthening applications a WC ratio of 1:1 to 10:1 is preferred. For grouting gas--and petroleum--bearing formations and wellbores, a WC ratio of 0.5:1 to 10:1 may be employed and for many such applications a ratio of 0.5:1 to 1.5:1 is preferred. Also a ratio of 0.3:1 to 10:1 may be employed, and preferably 0.4:1 to 1.5:1.

Additional materials in the grout are a dispersant, an accelerator and optional additives, the amounts of these described below being in weight percent solids based on the weight of cementitious material (CM) unless otherwise noted.

An effective amount of dispersant to disperse the CM may be up to 2%, and is preferably 0.1% to 1%, more preferably 0.2% to 0.5%. In grouting gas--and petroleum--bearing formations it is important to control viscosity of cement slurry which is being injected to facilitate pumping and penetration at increasing depths of the wellbore. Increased viscosity adversely affects penetration of cement into the formation. In this invention, it has been found that use of upto 2 percent by weight (based on cement) of a naphthalene sulfonate formaldehyde condensate (N2) as dispersant is effective to reduce viscosity and to provide desired control of viscosity. Furthermore, N2 has water loss reducing properties. Dispersants include polymers and lignosulfonates.

Also in such well cementing operations, it is necessary to avoid early set and hardening times which interfere with pumping and penetration at increased wellbore depths. Where this is a problem it is preferred to add an amount of a retarder effective to obtain desired longer set and hardening times. Retarders include lignins, gums, starches, weak organic acids and cellulose derivatives such as carboxymethyl hydroxyethyl cellulose. Some dispersants such as N2 and lignosulfonates also act as retarders.

Silica flour (finely ground silica) may be added in a proportion where the silica flour is not more than 50 percent of the total weight of silica flour, particulate slag and portland cement. The resulting composition is useful because of advantages of increasing compressive strength and durability.

To obtain the combined properties desired in the method of the present invention, it is essential to include an accelerator, in an effective amount to initiate or give the ultrafine slag sufficient hydraulic reactivity so that it sets and hardens in desired times, depending on the proposed applications. The accelerator may comprise an alkali or alkaline earth oxide, hydroxide or salt, which imparts the desired hydraulic reactivity to the ultrafine slag, or may comprise any other substance which is effective to provide or improve the hydraulic reactivity of the slag. NaOH is a preferred accelerator, particularly when used in an amount of 5 to 10% by weight of CM. NaOH may be used with optional further additives, such as sodium carbonate, to enhance the activation effect. It has been found that substitution of up to 40% by weight of the sodium hydroxide by Na₂ CO₃ is very effective, and preferably up to 20% of the NaOH is substituted. Such optional further additives also may be selected from alkali or alkaline earth oxides, hydroxides or salts, or from any other compound which functions to activate the slag. Also preferred as an optional further additive are alkali metal polysilicates, such as a lithium sodium polysilicate or a lithium polysilicate. Another optional further additive is sodium fluoride, which may be used in amounts up to 2%, preferably up to 1%, more preferably 0.1 to 0.5% by weight of the CM.

When an optional cement is used with the slag, particularly portland cement, in effect the accelerator is at least partly comprised therein due to the CaO content of the cement being capable of activating the slag. Thus, in some formulations in which a cement is mixed with the slag, a separate accelerator such as NaOH may be omitted. However, although the formulations using a mixture of slag and cement without a separate accelerator can have low set time and low settlement, hardening time may be substantially increased. Where such an increase is found, and a shorter hardening time is needed for the particular application, a separate accelerator may be used with the slag-cement mixture.

The slag employed in this invention is a by-product obtained in the blast furnace process of smelting iron ore to produce iron. The slag is produced by a conventional process, utilizing grinding and separating steps well known in the art. A typical dry composition range and two further examples of slag are shown in Table 2 (in weight percent):

                  TABLE 2                                                          ______________________________________                                         Compo-                                                                         sition SiO.sub.2                                                                              Al.sub.2 O.sub.3                                                                       CaO   MgO  FeO  S     Mn.sub.2 O.sub.3                  ______________________________________                                         Usual  30-40   8-18    35-50 0-15 0-1  0-2   0-2                               Range                                                                          Typical                                                                               36.4    16.0    43.3  3.5  0.3  0.5   <0.1                              Typical                                                                               35.5    11.4    39.4  11.9 0.2  0.2   --                                ______________________________________                                    

A high glass content, finely divided slag yields a grout having excellent sulfate resistance and readily controlled setting and hardening times in a relatively inexpensive formulation. High sulfate resistance is particularly important with regard to long term stability of the grouted formation. Grouting failures after five or ten years have been attributed to sulfate attack. The slag rich compositions of the present invention have long term stability in formations and are also useful in regrouting formations in which a previous grout has exhibited signs of failure. The grout is inexpensive because of the comparatively low cost of slag, a by-product of iron production.

Properties of specific types of MICROFINE cements which can be used in the present invention are shown in Table 3.

                  TABLE 3                                                          ______________________________________                                                     M1    M5       W3W0    M3                                          ______________________________________                                         Cementitious material                                                                        Slag    Slag/    Port- Portland                                                        Portland land                                            Fineness (cm.sup.2 /gm)                                                                      13000   9000     10000 11300                                     Sp. Gr. (gm/cm.sup.3)                                                                        3.00    3.00     3.06  3.06                                      Composition (wt %)                                                             SiO.sub.2     35.4    30.6     18.93 17.90                                     Al.sub.2 O.sub.3                                                                             16.0    12.4     18.93 4.93                                      Fe.sub.2 O.sub.3                                                                             0.3     1.1      3.78  3.48                                      CaO           43.3    48.4     61.57 61.63                                     MgO           3.5     5.8      2.96  2.59                                      K.sub.2 O     0.64    0.68                                                     Na.sub.2 O                     0.44  0.36                                      SO.sub.3      0.3     0.8      4.11  5.68                                      L.O.I. (Loss on Ignition)      2.40  2.90                                      1000° C.                                                                IR (Insoluble Residue)         0.45  0.42                                      TOTAL         98.8    99.5     100.00                                                                               100.00                                    ______________________________________                                    

M5 is a mixture of slag and portland cement which is ground to the indicated degree of fineness after mixing. Thus, the slag and cement are co-ground. W3W is portland cement ground with a polymeric grinding aid and M3WO is portland cement ground without a grinding aid. M3W and M3WO are useful to produce slag/cement mixtures by mixing with MICROFINE slag such as M1. The result is a mixture of individually ground MICROFINE cements which therefore were not co-ground. In some cases there are advantages in using such slag/cement mixtures over co-ground mixtures. Individual grinding can be done in an optimum way for the specific slag and cement, but co-grinding tends to be an optimum procedure only for one of the components. By means of individual grinding, a very high degree of fineness can be obtained in the mixture. Furthermore individual grinding enables production of mixtures in which the fineness of the mixture can be easily varied to suit particular needs.

High level of penetration into a tight formation associated with high permanence renders the present invention valuable in many applications. One example is radioactive waste storage in shafts deep in rock formations where the present invention may be employed to permeate the rock around the waste for secondary containment.

It is a feature of the invention that cementitious material having the fine particle size and distribution described is formulated in a composition producing high strength grout having a readily controlled set time.

While slag or slag plus cement are preferably used without inert filler material, in some instances it may be desirable to incorporate limited amounts of other solids meeting the particle size specification specified for slag herein. Such other solids are clay, bentonite, kaolin, vermiculite, limestone, silica flour, silica fume and other well known inert solids. The amount of these employed is to be minor so as not to reduce the strength of the set grout below desired values.

The dispersant is selected from materials used to disperse solids, preferably water-wetable solids, in aqueous systems. The dispersant serves to aid the penetration of water into the finely divided solids to produce a suspension of unassociated or unagglomerated particles. These dispersants are generally negatively charged or anionic electrolytes especially polyelectrolytes, such as polycarboxylates and polysulphonates. Examples include sodium ammonium salts of polymethacrylic acid, diisobutylenemaleic anhydride copolymer, copolymers of acrylic, methacrylic and maleic acids, organic phosphates, sulfonated naphthalene formaldehyde condensates, sulfonated natural products and other sulfonated polymer condensates.

The particle size of the materials is determined by a laser light scattering particles size distribution apparatus identified as a Microtrac® particles size analyzer (Leeds and Northrup Instruments, North Wales, Pa. 19454). Measurements are made in the 0.7 to 125 micrometer range and are presented in terms of the volume of particles in size channels having a size ratio of approximately 1.4 between channels. Results are given as the percent larger than the stated size for each channel limit and the calculated volume surface area of the sample in square meters per cubic centimeter. The volume surface area can be converted to the specific surface, in square meters per gram, by dividing by the density of the material. Portland cement density is considered 3.15 grams per cubic centimeter as in ANSI/ASTM standard C 104-78a; slag density is considered 2.92 grams per cubic centimeter.

Set time and settling are determined by the following general procedure:

1. The components are mixed in a plastic cup, as described in the hereinbelow Examples.

2. the mixture is colloidally agitated for 10 seconds by a high speed mixer.

3. the cup is tilted periodically while the CM surface is observed. When there is no flow or gross motion of the CM surface while the cup is tilted to 45 degrees the time is noted; this is the set time. Settling of the CM is observed; the percent of the total volume present as clear or cloudy surface liquid is reported as percent settlement.

Hardness development is monitored by measurement of the compressive strength and is reported along with the time of the measurement elapsed after sample preparation. The strength measurement employs a handheld penetrometer (Soiltest CL-700 Pocket Penetrometer, Soiltest Inc., Chicago, Ill.) and follows the manufacturer's instructions. The penetrometer is held by its handle with the piston at right angles to the CM surface. With steady pressure the piston is pushed into the CM to the depth of the calibration groove about 1/4 inch from the end of the piston. The compressive strength is read on the scale of the instrument.

It is advantageous to utilize slag as the cementitious material rather than portland cement in the grouting method and composition of the present invention, for several reasons. First, the slag component is available commercially in very finely divided form, such as the product described above which has a specific surface area of 14,000 cm² /g; the slag is less costly, and offers the advantage of being non-polluting. However, the hydraulic reactivity of such slag is low, and a number of the intended applications require a reasonably fast set time and hardening time, that is, attaining desired strength in a reasonable time. Furthermore, in number of the intended uses for the present method and composition, it is important to obtain a low water permeability in the grouted formation. Thus, in such uses, a low percent settlement is desired (so that all the pores and openings in the formation being grouted are filled). The grouting composition desirably should exhibit a set time of below 6 hours, but not less than 0.5 hour. Preferably the set time is from 1 to 5 hours, more preferably from 1 to 4 hours and most preferably from 1 to 2 hours.

A desirable hardening time for the present invention is obtained when the strength of the grout is at least 4.5 kg/cm² within 20 hours, preferably in less than 10 hours and more preferably in less than 6 hours.

The percent settlement desired depends on the intended use, and normally should be below 50% (volume). It is more desirable for percent settlement to be below 45%, with a settlement of 0-35% being more preferable and 0-10% settlement being most preferable.

However, the particular application of the present method and composition will determine the best choice of properties. For example, in situations involving water containment such as stabilizing or containing hazardous waste, low percent settlement is desired and for this purpose the water/CM (WC) ratio may be chosen to be low in water. For uses which involve strengthening formations where water containment is not a problem, the WC may be chosen to be higher in water. A higher ratio means use of less of the CM component and therefore is less costly.

In addition to requirements imposed by the intended use, the nature of the formation must be considered. A formation having larger openings or pores to be grouted can be grouted with a composition having a low WC but a formation into which the grout can penetrate only with difficulty, even with use of high pressure pumps, may require a higher WC to lower grout viscosity.

It is an advantage of the method and composition of the invention that the grout can be formulated to have the most desirable combination of these properties for the particular intended use and nature of the formation. The components of the grout may be selected to modify the properties as desired, and modification is also possible through use of optional additives.

For uses of the method in stabilizing or strengthening formations, a low WC is needed where high strength is needed in the grouted formation. However, in such uses, the permeability of the resulting grouted formation is usually is not a problem so that a low permeability does not have to be achieved. Furthermore, many situations involving stabilization do not also call for high strength in the formation. For example, if a formation is to be stabilized for tunnel excavation, some strengthening of the formation is desired but not so as to make excavation difficult. As a result, a higher water proportion in the WC can be employed. For stabilizing and strengthening formations, it is preferred in the method and composition of the present invention to use a WC in the range of 1:1 to 10:1 by weight.

When the method is used to stabilize hazardous waste or nuclear materials, an important requirement is low permeability of the resulting grouted formation. In such uses, or other uses involving containment of water, it is desirable to employ a WC in the range of 0.5:1 to 2:1 by weight. Normally, the appropriate grout would give permeability rates of from 10⁻⁶ to 10⁻⁹ cm/sec rate of flow of water.

The ultrafine ground slag used in the present method and composition is advantageous over the use of ordinary portland cement because it is available in a much finer particle size distribution at lower cost. As a result, compared with portland the present slag enables the grouting operation to proceed with a grout having considerably lower viscosity and particle size than known grouts.

Because of its large particle size, ordinary portland will not penetrate course sand. MICROFINE portland/slag (M5) will penetrate fine sand at 130 ml in 5 minutes as compared with the present invention (M1) which will penetrate the same fine sand at 600 ml in 11 minutes. This demonstrates the considerable advantage of the present invention over existing technology.

In previous attempts to use microfine ground slag in combination with cement for grouting, there have been problems in obtaining a composition which had a low enough viscosity to meet fast penetration requirements and which also had a combination of the other desired properties discussed above. It was known (see the above-mentioned W. J. Clarke ASCE preprint 84-023) to combine MICROFINE cement in combination with sodium silicate for underground water control. However, this is a two component system (two separate mixtures in appropriate containers required at the site) as compared to the more effective one component mixture used in the present invention. Furthermore, it was necessary to include portland cement in such mixtures for hydraulic reactivity and the grout was not strong (it is weakened by the high content of sodium silicate). Although it was possible to obtain 0% settlement with such grouts, they have a problem of very fast set time, typically 1-3 minutes, which interferes with or prevents injection of grout into formations.

It has been found in the present invention that set time, hardening time and percent settlement properties can be obtained within the present desired limits, and can be further lowered by a specially preferred method of formulating the grout composition. It has been discovered that properties can be improved by following a special sequence of mixing components of the composition. In this embodiment of the invention, the dispersant component is first added to water and mixed to the extent necessary to form a solution or suspension, which will be referred to herein as a first mixture. To this first mixture there is then added the microfine slag component or the mixture of microfine slag with a cement, thereby forming a second mixture, which can be stirred or agitated to the extent necessary to insure contact of the dispersant with a substantial portion of the slag particles. Then, the accelerator is added to the second mixture. The resulting composition is subjected to strong agitation such as colloidal mixing or mixing in a high speed blender, to break up particle agglomerates. Optional additional dispersants are added at the time of forming the first mixture, and additional optional accelerators are added at the time of adding the specified accelerator to the second mixture.

In case no separate accelerator additive is used, and this function is fully served by mixing very finely divided portland cement with the slag, the preferred sequence for mixing the components is to first add a dispersant to water to form a first mixture. This mixture may be stirred or agitated if necessary to dissolve or disperse the dispersant. Then the mixture of slag and portland cement is added to the first mixture to form a second mixture. This second mixture may be immediately subjected to strong agitation as described for the embodiment in which only slag is used as the CM.

It has been found that the preferred sequence of addition provides enhanced and advantageous properties in the grout which then is ready for use. If the accelerator is added to the water and dispersant before addition of slag it is believed that there is a detrimental effect on the dispersant. Adequate dispersing of the slag particles is not achieved and agglomerates become a problem. Reversing the preferred sequence of mixing in these ways will prevent attaining optimum properties in the grout. However, in some cases it may be necessary to add components in a way not in accordance with the preferred sequence of addition, for example in cases where an optional additional accelerator is used. It is also undesirable to add the dispersant last, i.e. after the accelerator is added.

In another embodiment of the invention, it has been found that an improvement in one or more of the properties of set time, hardening time or percent settlement can be obtained by selection of sodium hydroxide as the accelerator, in a particular proportion range. The use of sodium hydroxide as an accelerator for slag is known. However, it has been thought necessary to minimize the amount of sodium hydroxide both for reasons of cost and because of expected adverse effects on the grout or on the formation or structure which is grouted. However, surprisingly, it has been found that a decrease in one or more of the set time, hardening time or percent settlement can be achieved by using at least 5% sodium hydroxide by weight of the slag. Further improvements can be achieved by increasing sodium hydroxide up to about 10%. Higher amounts than 10% may be utilized but are not economical and very high amounts may affect the formations. The use of 5-10% of sodium hydroxide enables a higher WC to be employed while still obtaining grout properties within desired limits. Up to 40% by weight of the sodium hydroxide may be substituted by Na₂ CO₃ with excellent results. Preferably up to 20% by weight of the sodium hydroxide is replaced, when Na₂ CO₃ is used.

The present invention is illustrated in the drawings wherein FIG. 1 is a ternary phase diagram illustrating the relative proportions of calcium, aluminum and silicon oxides. Areas are shown representing blast furnace slag 1 with M1 microfine slag 2 located therein, M5 microfine slag/cement 3, portland cement 4, fly ash 5 and alumina cement 6.

A dam curtain grouting is schematically shown in FIG. 2 in which a dam 8 holds back water 9. Curtain grouting 10 is located within formation 11 and serves to contain water permeating from dammed water 9. The curtain grouting may be an older portland cement curtain through which water now permeates. The openings in the original grouting are closed by grouting in accordance with the method of the present invention so that the original curtain grouting is restored to an impermeable state.

FIG. 3 illustrates strengthening a formation beneath a foundation 14. Formation 15 is grouted by the method of the present invention.

Nuclear waste containment is illustrated in FIG. 4. Nuclear waste 20 is contained in containers 16 immobilized by portland cement 17. The immobilized containers are contained within shaft 19 which may be lined with metal or concrete. The shaft is shown out of proportion but actually is a very deep shaft in rock formation 18. The rock around the shaft is grouted 21 for secondary containment protection.

FIG. 5 illustrates stabilization of hazardous waste. Hazardous waste 26 is present in a formation 25. Surface water and water from the water table flows in the direction of the arrows, and leaches the hazardous waste, forming hazardous waste plume 27. The hazardous waste is contained by curtain grouting 28 to minimize further contamination.

FIG. 6 schematically depicts a tube-a-machette system for injection of grout into a formation, which may be employed in the method of present invention. A grout pipe 30 is installed in borehole 37. Lean cement grout 41 fills the space between grout pipe 30 and the wall of borehole 37. Grout pipe 30 has a plurality of ports 32 closed by tight-fitting rubber sleeves 33, acting as a check valve. Sleeve 33 is shown in closed position 34 and open position 35. Injection tube 31 moves double-ended packer 39 which isolates individual ports 32, permitting injection through isolated ports at specific depths. A grouting composition used in the present invention is injected through pipe 31 as shown by arrows. The grout is pumped under pressure which moves sleeve 33 away from port 32. The grout under pressure breaks through lean cement grout 41 into passage 42. In this way the grout is injected into the formation as shown by arrows, and forms a spreading grout region 40.

An alternative procedure is to drill the borehole while inserting a 3 inch steel casing during drilling. Upon completion of the borehole, the drill is removed and the steel casing remains in the borehole. The interior of the casing is filled with a lean cement grout (high water content). The above-described tube-a-machette is inserted into the casing while the lean grout is fluid, and then the casing is removed. The lean grout is allowed to harden, whereupon it seals the annular space around the tube-a-machette. The lean cement grout fractures when subjected to the impact of high pressure grout being injected through the ports of the tube-a-machette.

The injection procedure is used to form a grout curtain upstream of the hazardous waste plume. This may be done by boring a row of sufficiently deep holes, such as 80-100 feet deep, in a single row, spaced so that the spreading grout from each borehole will overlap with the next. Another procedure is to space boreholes in a single row on 20 foot centers. Type V portland cement is injected into those boreholes. Between each such borehole a centered further borehole is drilled and injected in accordance with the above procedure using the method of the present invention. The space between the portland cement injected borehole and the slag injected borehole can again be split with a further centered borehole injected in accordance with the present method. To further contain the flow of water, a second or a second and a third row of injected boreholes can be formed thus establishing the grout curtain. The ends of the grout curtains can be extended in a downstream direction to enclose the sides of the hazardous waste site. It is also possible, where necessitated by hazardous waste conditions, to entirely enclose the perimeter of the hazardous waste site with such grout curtains and in some situations grout can also be extended beneath the hazardous waste site.

The method of the present application is of particular use in cementing wellbores and in grouting porous gas--and petroleum--bearing formations, i.e. formations in which hydrocarbons such as natural gas and petroleum are found. These geological formations containing hydrocarbon deposits include porous reservoir rocks, sand, shale, sandstone, and limestone. The method of the invention has advantages in well drilling and production operations, and especially for primary or remedial cementing of a wellbore, such as squeeze cementing.

Specific techniques for primary and remedial cementing are described in the above mentioned "Worldwide Cementing Practices" publication. Primary cementing involves introduction of cement into the space between the outside of the steel casing of the well and the borehole wall (or the inside of a previously set casing if a new casing was introduced). Cement slurry is pumped down the entire length of the casing, out the borehole joint and into said space. Remedial cementing concerns procedures to remedy undesired conditions in a well such as to shut off water flows or repair casing damages. The most common remedial cementing procedure is called squeeze cementing.

Squeeze cementing has been described in the above publication as being the process of applying hydraulic pressure to a cement slurry to (1) force or "squeeze" the slurry into the desired location and (2) force water from the slurry after placement to create a mass which will remain in place and harden to provide a seal. The publication lists some reasons why squeeze cementing is done, as follows:

1. Repair of a faulty or inadequate primary cement job.

2. Shut off unwanted water or gas.

3. Isolate a zone prior to perforating for production.

4. Abandon a nonproductive zone.

5. Seal off thief zones or lost circulation during drilling,.

6. Repair casing leaks.

7. Modify injection profile in injection wells.

8. Provide initial seal for a liner (tack and squeeze).

It is known in the art that there are difficulties in achieving success in such cementing operations due to the difficult conditions encountered in wells. Portland cement has been used in the typical cement slurry for well cementing, but has disadvantages because of a particle size larger than pore diameters of the formation, and because of relatively short thickening or set times. The latter is a special problem in deeper wells having an increased temperature with depth, causing too rapid thickening which adversely affects pumping and placement of the cement. It is also important for the hardened cement to have sufficient strength.

MICROFINE cements used in the present method are cementitious grouting materials composed of ultrafine particles of slag and portland that exhibit excellent penetrability, strength and durability suitable for squeeze cementing of oil well matrices, especially for gas and water control.

Application of ultrafine cements in squeeze cementing is enhanced by ultrafine particle size for penetration of medium sands and finely cracked rock in oil well matrices. Filtration properties (ability to hold water) are excellent because of ultrafine particle size and addition of one percent dipsersant lowers viscosity and extends initial hardening time at high temperatures in the oil well matrix.

The present method therefore is suitable for the following squeeze cementing applications:

Reduce High GOR (Gas/Oil Ratio)

Control Excess Water

Repair Casing Leaks

Seal Off Thief Zones

Protection Against Fluid Migration

The following properties of the ultrafine cement allow penetration of the oil well matrix.

(a) Penetrating Power: MICROFINE particle size (maximum 2 percent at 2 micron) allows the grout to penetrate fine sands and finely cracked rock in well matrix.

(b) High Hardened Strength: MICROFINE grains are naturally activated with portland to rapidly harden to high strength.

(c) Excellent Durability: after hardening by hydrating, the ultrafine cements acquire high impermeability which protects them from sulfates and chlorides to insure high durability.

(d) Long initial Hardening Time: combination of ultrafine slag and portland provides long fluid time at high temperature and pressure for maximum penetration of oil well matrix.

Application of the ultrafine cements in squeeze cementing is enhanced by ultrafine particle size for penetration of medium sands and finely cracked rock in oil well matrices. Filtration properties (ability to hold water are excellent because of ultrafine particle size and addition of dispersant lowers viscosity and extends initial hardening time at high temperatures in the oil well matrix.

The MICROFINE slag/cement has excellent set time, initial hardening time and viscosity in well cementing. Longer set and hardening times at high temperature result from larger quantities of blast furnace slag in the M5 ultrafine cement. The longer initial hardening time allows for down hole cementing for deep wells. Appropriate accelerators and retarders may be used for varying well depths and temperatures.

The following oil well squeeze cementing operations (besides others) may be performed with M5 MICROFINE cement:

Abandonment

Fine sands and finely cracked rock around non-commercial well zones may be sealed with M5. A prudent practice in abandoning a set of perforations is to set a drillable squeeze packer and attempts to squeeze the abandoned perforations with a low fluid loss cement at less than fracturing pressure.

Block Squeeze

Block squeeze is used before perforating for production to prevent fluid migration from either above or below. M5 will penetrate blocked matrix better than ordinary portland to more efficiently prevent fluid migration.

Squeeze Unwanted Water

Water is an integral part of all porous rock and is present in most oil and gas bearing formations. Migration of water may be controlled when larger quantities of low viscosity M5 slurry penetrate the matrix pore spaces at less than fracturing pressure.

Reducing GOR (Gas Oil Ratios)

During the life of a well the GOR may increase beyond the economic limit, necessitating remedial action. A common procedure is to squeeze off all the perforations in the oil and gas zones which may be done with M5 and then perforate at selected intervals.

Thief Zones

M5 may be used to seal off thief zones in the upper section of a slotted gravel pack liner. Using a combination of M5 and microflour, a thief zone may be sealed to increase production.

The ultrafine cements have been found to be significant additions to cementitious material for oil well cementing because of the following inherent properties:

1. Ultrafine particle size allows penetration of fine sands and finely cracked rock in the oil well matrix.

2. Inherent long initial hardening time because of high ultrafine slag content may be enhanced with polymer accelerators and retarders.

3. Low clear settlement, non hard settlement and medium viscosity from ultrafine particle size may be improved with viscosity reducers and dispersants.

4. Inherent low slurry density and high hardened strength from high ultrafine slag content allows penetration of microchannels caused by gas migration.

Fundamental ultrafine particle size, long initial hardening time and high hardened strength of the ultrafine cements may be enhanced by the use of modern polymer technology accelerators, retarders, dispersants and fluid loss polymers. Physical properties of the ultrafine cement may also be improved by the addition of silica fume, bentonite, sodium silicate and silica flour.

As mentioned above, M5 cement is avialble in the desired particle size. In some applications it will be advantageous to further grind all or part of the cement/slag, especially in the field, i.e. in locations near the formation to be grouted.

The portland cement component may be further ground prior to mixing with slag by grinding particulate portland cement having a particle size wherein less than 10 wt. percent of the particles are larger than 10 micrometers in diameter to a particle size wherein less than 2 wt. percent of the particles are larger than 10 micrometers in diameter, in a tower mill at or near the location of said formation to be grouted.

Also, particulate slag and particulate portland cement may be co-ground to a particulate size wherein less than 2 wt. percent of the particles are larger than 10 micrometers in diameter in a tower mill at or near the location of said formation to be grouted.

Mixtures of 75% MICROFINE slag and 25% MICROFINE portland are especially useful in oil well cementing and can be produced by such tower mill grinding.

Apparatus and techniques for Tower mill grinding are known. Typically dry and wet Tower Mills are approximately 10 feet high and 2 feet diameter, charged with 1/2" stainless steel or ceramic balls, all internally rubber lined with a screw rotating at 35-85 rmp.

The following examples are included to illustrate the invention.

Definitions of Symbols Used in the Examples

    ______________________________________                                         W     Water                                                                    CM    Cementitious material                                                    M1    Slag ground to 14,000 cm.sup.2 SSA                                       M3W   MICROFINE portland cement ground with a polymer                                grinding aid to 11,300 cm.sup.2 /g SSA                                   M3W0  MICROFINE portland cement ground without a grind-                              ing aid to 10,000 cm.sup.2 /g SSA                                        M5    MICROFINE portland/slag co-ground to 8,880 cm.sup.2 /g                         SSA                                                                      C6    Dispersant, 3000 MW polyacrylic acid copolymer                           N2    Dispersant, naphthalene sulfonate formaldehyde                                 condensate                                                               FL    Accelerator, a 50% aqueous solution of calcium nitrate                         (Sika Corp., Lyndhurst, N.J.)                                            HE    Accelerator, a 30% aqueous solution of calcium chloride                        (Sika Corp, Lyndhurst, N.J.)                                             D     Dispersant                                                               DCI   Corrosion inhibitor, a 30% aqueous sodium nitrate                              solution (W. R. Grace Co.)                                               4180  Dispersant, a copolymer of acrylic acid                                  M     MICROFINE slag, slag/cement or portland cement                           WC    Weight ratio of water to cementitious material                           A     Accelerator                                                              LiS   Accelerator, lithium sodium polysilicate, available                            from Lithium Corporation of America, (lithsil S), a                            typical analysis of this product being:                                        Li.sub.2 O (1.8) Na.sub.2 O (1.2) SiO.sub.2 (19.6), 22.6% solids         Li6   Accelerator, lithium polysilicate, available from                              Lithium Corporation of America, (lithsil 6), a typical                         analysis of this product being:                                                Li.sub.2 O (2.2) SiO.sub.2 (20.7), 22.9% solids                          ______________________________________                                    

Example 1 gives data on the properties of grout injected by the method of the invention. Neat grout is the grout in absence of sand, such as when injected into a rock formation.

In Examples 2 to 7, compositions were prepared with components as shown under "COMPONENTS-MIXING ORDER"; The components were mixed in the order indicated by reading the symbols from left to right, except as otherwise explained. For example, in Example 2, run 70a, 100 g water was mixed with 0.5 g C6 dispersant, and 50 g M1 slag then were added with mixing. 5 g NaOH (50% by weight) were added and the mixture was agitated in a high speed blender. For simplicity, amounts of water and slag or cement are shown as the proportion of water to cementitious material by weight, and all other components as a percentage of the weight of total cementitious material.

Measurements of set time and strength are given for the condition of the grout at the time of the measurement and elapsed time is reported as the period from the end of mixing the components until the time of the measurement.

Components were mixed at ambient temperatures, generally normal room temperature except where different temperatures are shown.

A typical experimental procedure is outlined for run 76b in Example 5 as follows;

1. 100 grams of water are weighed into a 4 ounce plastic cup with cap. pH and temperature of water an recorded using a portable Hach One pH meter model 43800-00 by Hach Company, Loveland, Colo.

2. Plastic cup is tared and 5 grams of C6 dispersant are added to water and mixed. pH and temperature are recorded.

3. 50 grams of M1 microfine cement are added to water, cap applied, sample shaken and pH/temperature recorded.

4. 5 grams of 50% NaOH are added, shaken and pH/temperature recorded.

5. 5 grams of 100% LiOH are added, shaken and pH/temperature recorded.

6. Contents of cup are shaken, poured into Osterizer Model 869-15H and blended at high speed for 10 seconds. pH/temperature recorded and cup is labeled, dated, timed.

7. Set time 12 hr is measure of initial set as surface of M2 not moving when cup is tilted 45 degrees.

8. Measure unconfined compressive strength using Soiltest Pocket Penetrometer CL-700:at increasing times until strength exceeds 4.5 kg/cm² . . . the limit of testing instrument.

9. Percent Settlement is measured after 12 hours as linear measurement from top of water to top of M1 surface as percent settlement, e.g., 1/2 supernatant and 1/2 M1 is 50% settlement.

EXAMPLE 1

    ______________________________________                                         Material Tested                                                                ______________________________________                                         Ottowa 20-30 sand                                                                             U.S. Silica Company, IL                                         MC-100 MICROFINE                                                                              Blue Circle Atlantic                                            cement (M1)    Baltimore, MD                                                   MC-500 MICROFINE                                                                              Onoda Cement, Tokyo, Japan                                      cement (M5)                                                                    Ordinary Portland                                                                             (OP) Chicago, IL                                                M3WO MICROFINE Heracles Cement, Athens, Greece                                 portland (223)                                                                 M3W MICROFINE  Heracles Cement, Athens, Greece                                 portland (224)                                                                 Particles Size and Composition                                                 ______________________________________                                    

                  TABLE 4                                                          ______________________________________                                         Particle Size Distribution of Ottowa 20-30 Sand, M1, M5, OP                    Grain Size (mm)                                                                Percent Finer (wt)                                                                         20-30 Sand                                                                               M1      M5     OP                                        ______________________________________                                         100         0.840     0.0070  0.0100 0.070                                     80          0.550     0.0040  0.0057 0.027                                     60          0.520     0.0026  0.0037 0.017                                     40          0.500     0.0017  0.0023 0.008                                     20          0.480     0.0010  0.0014 0.003                                      0          0.420     0.0007  0.0008 0.009                                     ______________________________________                                    

Neat Sample Preparation

1. Add 5 grams of N2 to 500 grams of water and mix.

2. Add 500 grams of M5, shake and disperse in Hamilton Beach high speed mixer for one minute.

3. Pour mix into pre-slit PVC pipe, one inch ID by one foot long.

4. After desired curing time, open slits, remove sample and cut in 2 inch lengths, trim and smooth end faces.

Grout Injection Mold Preparation

1. Use ASTM Standard D4320-84 for grout injection mold set up.

2. Use three piece split mold, 38 mm ID by 96 mm long segmented 120 degrees each, rubber gasket and glued along segments.

3. Three hose clamps are spaced equally along cylinders to compress gaskets.

4. End of cylinders are seated with round rubber gaskets, placed in end plates ready for filling with sand.

5. To allow easy flow of grout without moving sand particles, place perforated plastic disc and filter mesh in bottom of mold.

6. Air dried 20-30 Ottowa Sand is poured into mold in three equal layers compressed at each layer with a 320 gram cylinder.

7. Using a hand-held Burgess Vibrotool, each layer of sand is vibrated for one minute until cylinder is filled.

8. A filter mesh (70 mesh polyester screen) and a perforated disc (12 1/16th inch diameter holes) and rubber gasket are placed on the sand. End plate is secured by tightening tie bolts.

9. Samples prepared by this procedure give consistant results in void ratio (average 0.52) and relative density at this void ratio is 80%.

Grout Injection Procedure

1. Samples are wetted by injection water through sample bottom at 1 psi for one minute and soaked for 15 minutes.

2. One liter batches of M5 were prepared with one percent N2 on M5 and 1:1 WC ratio. Batch mixed in a Waring Blender for one minute before transferring to a two liter pressure tank.

3. Grout injection set up consists of six sample cylinders, holding tank and pressure regulator.

4. Grout flow is started by placing 2 psi air in holding tank. Grout flow is stopped when 200 ml is passed through each sand cylinder. Samples are held in molds for three days curing.

Unconfined Compression Test

1. Use ASTM Standard D4129 for testing M5 with strain rate of 0.2 mm/min.

2. Unconfined compressive strength of neat M5 in 3, 7 and 28 days is outlined in Table 5.

3. Effect of curing time on strength of neat M5 and OP is shown in Table 6.

4. Effect of curing time on strength of M5 grouted sand at various WC ratios is shown on Table 7.

                  TABLE 5                                                          ______________________________________                                         Stress Strain Data for Neat Grout                                              M5 (WC 1:1, 1% N2 on M5)                                                       Strain Rate 0.2 mm/min                                                                      3 day       7 day   28 day                                        ______________________________________                                         Strength (kg/cm.sup.2)                                                                      68          163     234                                           Strain (%)   1.30        1.05    0.95                                          ______________________________________                                    

                  TABLE 6                                                          ______________________________________                                         Effect of Curing Time on Strength of Neat M5 and OP.                           M5 (WC 1:1, 1% N2 on M5)                                                       Strain Rate 0.2 mm/min                                                                     3 day    7 day    28 day  60 day                                   ______________________________________                                         Strength (kg/cm.sup.2)                                                         M5          57       170      240     290                                      OP          80       133      190     210                                      ______________________________________                                    

                  TABLE 7                                                          ______________________________________                                         Effect of Curing Time on Strength of Grouted Sands.                            M5 (WC 1:1, 2:1, 3:1, 1% N2 on M5)                                             Strain Rate 0.2 mm/min                                                                     7 day    14 day   28 day  60 day                                   ______________________________________                                         Strength (kg/cm.sup.2)                                                         M5 (WC 1:1) 110      128      162     202                                      M5 (WC 2:1)  27      36       49      63                                       M5 (WC 3:1)  8       13       18      24                                       ______________________________________                                    

Creep Test Procedure

1. Creep test of M5 grouted sand was performed using standard procedures on creep testing equipment.

2. Percent Strain verses time of M5 grouted sand is shown in Table 8.

                  TABLE 8                                                          ______________________________________                                         Creep of M5 Grouted Sand                                                       Strain (%)                                                                     Days  0      20     40   60   80   100  120  140  160                          ______________________________________                                         D =   .1     .19    .20  .22  .25  .26  .27  .28  .29                          0.7                                                                            D =   .65    .68    .70  .72  .73  .74                                         0.8                                                                            ______________________________________                                          D = Percent of failure load of M5 grouted sand                           

Permeability Test Procedure

1. Permeability of M5 grouted sand was performed using standard procedures with triaxial permeability cells.

2. Effect of curing time on permeability of M5 grouted sand at 1:1 and 3:1 WC ratio is shown in Table 9.

                  TABLE 9                                                          ______________________________________                                         Effect of Curing Time on Permeability of Grouted Sand                          M5 (WC 1:1 and 3:1, 1% N2 on M5)                                               Permeability (cm/sec)                                                                       4 day   7 day   20 day                                            ______________________________________                                         WC 3:1         10.sup.-5 10.sup.-5.1                                                                            10.sup.-5.2                                   WC 1:1         10.sup.-7.2                                                                              10.sup.-7.4                                                                            10.sup.-7.5                                   ______________________________________                                    

EXAMPLE 2

In all compositions of this examples (except for run 701, see note (6)), the dispersant was C6 in an amount of 1.0% based on the weight of the slag component (in run 70c it was 1.1%). The accelerator in all runs was NaOH in % by weight of CM as shown.

    __________________________________________________________________________         COMPO-                                                                         NENTS &              STRENGTH                                                                              SETTLE-                                            MIXING       NaOH                                                                               SET-                                                                               S: kg/cm.sup.2                                                                        MENT                                           RUN ORDER CM WC  %   hours                                                                              H: hours                                                                              vol. %                                         __________________________________________________________________________     70al                                                                               WDMA  M1 2:1 5   3   S: >4.5                                                                               50                                                                      H: 18                                                 70a WDAM (1)                                                                             M1 2:1 5   9   S- >4.5                                                                        H: 18  50                                             70b WDAM (2)                                                                             M1 2:1 5   9   S: >4.5                                                                        H: 18  50                                             70c WDMA (3)                                                                             M1 2.2:1                                                                              5.6 9   S: >4.5                                                                        H: 31  50                                             70h WDMA  M1 1:1 5   1   S: <4.5                                                                        H: 4    0                                             70i WDMA  M1 0.9:1                                                                              5   1.1 S: >4.5                                                                        H: 4    0                                             70j WDMA  M1 0.8:1                                                                              5   1   S: >4.5                                                                        H: 4    0                                             70k WDMA (4)                                                                             M1 0.9:1                                                                              5   3   S: >4.5                                                                        H: 18  -- (5)                                         70l WDMA (6)                                                                             M1 1:1 5   2   S: >4.5                                                                        H: 18   2                                             __________________________________________________________________________      (1) 1.0% FL accelerator added, and to avoid precipitating it, both FL and      NaOH were added before M1.                                                     (2) 1.0% HE accelerator added, and to avoid precipitating it, both HE and      NaOH were added before M1.                                                     (3) 5.6% CaO accelerator added with the NaOH after M1.                         (4) 10.0% DCI added after M1.                                                  (5) no observation made.                                                       (6) 4180 dispersant in an amount of 1% was used in place of C6.          

COMMENTS

Runs 70 a1, a and b: Accelerators HE and FL caused precipitation and opalescence, therefore, NaOH was added before M1. 50% settlement and extended set time are unsatisfactory . . . CaO gave same results.

Runs 70 h to k: Low WC at or lower than 1.1 is required for hazardous waste containment to obtain 0-5% settlement. Low settlement and complete void filling are required to obtain very low formation permeabilities (10⁻⁶ to 10⁻⁸ cm/sec) for hazardous waste and nuclear waste containment.

EXAMPLE 3

The effect of different accelerators on different CM components is compared. In runs 70 a-d the dispersant was 1%, C6, and in 70 e-i it was 1% N2.

    __________________________________________________________________________         COMPO-                                                                         NENTS &               STRENGTH                                                                              SETTLE-                                           MIXING       NaOH                                                                               SET- S: kg/cm.sup.2                                                                        MENT                                          RUN ORDER CM  WC %   hours                                                                               H: hours                                                                              vol. %                                        __________________________________________________________________________     74a WDMA  M1  2:1                                                                               10  2.5  S: >4.5                                                                               10                                                                      H: 26                                                74b WDMA (1)                                                                             M1  2:1                                                                               10  2.0  S: >4.5                                                                                5                                                                      H: 25                                                74c WDMA (2)                                                                             M1  2:1                                                                               10  >4.0 S: >4.5                                                                               25                                                                      H: 24                                                74d WDMA (3)                                                                             M1  2:1                                                                               10  2.0  S: >4.5                                                                                5                                                                      H: 24                                                74e WDMA (1)                                                                             M5  2:1                                                                               0   2.0  S: >4.5                                                                               35                                                                      H: 91                                                74f WDMA (4)                                                                             M5  2:1                                                                               0   >10  S: >4.5                                                                               35                                                                      H: 37                                                74g WDMA (3)                                                                             M5  2:1                                                                               0   10.0 S: >4.5                                                                               45                                                                      H: 90                                                74h WDMA (5)                                                                             M1 &                                                                               5:1                                                                               0   0.02 S: >4.5                                                                                0                                                      M3W        (1.2 Min)                                                                           H: 90                                                          1:1                                                                  74i WDMA (5)                                                                             M1 &                                                                               5:1                                                                               0   0.02 S: >4.5                                                                                0                                                      M3WO       (1.3 Min)                                                                           H: 88                                                          1:1                                                                  __________________________________________________________________________      (1) 1% LiOH accelerator added after CM.                                        (2) 1% sodium tetraformate added before CM (since a viscous black              precipitate forms when added after CM).                                        (3) 1% NaF was added after CM, as an accelerator.                              (4) 1% sodium tetraformate was added after CM.                                 (5) A 2 component system was prepared; as a first component, 60 g water,       0.2 g N2 dispersant and 20 g CM as shown above; as a second component, 38      g Na.sub.2 SiO.sub.4 and 40 g water. The two components were then mixed. 

COMMENTS

Runs 74 a-d: The effect of the additional accelerators may be masked by the high (10%) NaOH content (see Example 5, runs 76 b-d where NaOH is 5%).

Runs 74 e-g: Accelerators as 1% of M5 did not decrease hardening time or % settlement as required.

Runs 74 h-i: These rums are included for comparison, and represent use of a 2 component high Na₂ SiO₂ content system not in accordance with this invention. It is of interest that M3W and M3WO microfine portland cements operated satisfactorily with 50% M1 in the two component system with Na₂ SiO₂.

EXAMPLE 4

This was a study of the effect of one percent increments of NaOH on compositions employing M1 as CM.

    __________________________________________________________________________         COMPO-                                                                         NENTS &              STRENGTH                                                                              SETTLE-                                            MIXING       NaOH                                                                               SET-                                                                               S: kg/cm.sup.2                                                                        MENT                                           RUN ORDER CM WC  %   hours                                                                              H: hours                                                                              vol. %                                         __________________________________________________________________________     75a WDM   M1 2:1 0   8 (1)                                                                              S: >4.5                                                                               40                                                                      H: 168                                                75b WDMA  M1 2:1 1   6 (1)                                                                              S: >4.5                                                                               70                                                                      H: 44                                                 75c WDMA  M1 2:1 2   6 (1)                                                                              S: >4.5                                                                               70                                                                      H: 44                                                 75d WDMA  M1 2:1 3   6 (1)                                                                              S: >4.5                                                                               60                                                                      H: 44                                                 75e WDMA  M1 2:1 4   6 (1)                                                                              S: >4.5                                                                        H: 44  60                                             75f WDMA  M1 2:1 5   6 (1)                                                                              S: >4.5                                                                               45                                                                      H: 16                                                 75g WDMA  M1 2:1 6   5   S: >4.5                                                                               35                                                                      H: 15                                                 75h WDMA  M1 2:1 7   5   S: >4.5                                                                               35                                                                      H: 15                                                 75i WDMA  M1 2:1 8   4   S: >4.5                                                                               25                                                                      H: 15                                                 75j WDMA  M1 2:1 9   4   S: >4.5                                                                               20                                                                      H: 14                                                 75k WDMA  M1 2:1 10  4   S: >4.5                                                                               15                                                                      H: 14                                                 __________________________________________________________________________      (1) Only a part (at the bottom) of the CM set.                           

COMMENTS

Runs 75 a-g: NaOH is an important accelerator for use with pure M1 to initiate the alkali activated slag reaction. However, severe settlement was obtained below 5 percent NaOH, with a cloudy supernatant, long set times and long hardening times.

Runs 75 g-k: Increasing NaOH to 5% gave significant improvements, and use of 7-10% NaOH resulted in unexpected clear supernatant, reduced settlement to 15%, reduced set time to 4 hours and reduced hardening time to 14 hours. These are very significant improvements.

EXAMPLE 5

In runs 76 b-d, additional accelerators were tested for effect on M1 in the presence of NaOH at a 5% level. The effects of NaOH at varying WC ratios and different dispersant amounts were studied (runs 76 e-g and i). In run 76h the sequence of addition of NaOH was tested by adding NaOH before M1. Runs 76j and k test compositions having microfine portland cement as the sole CM; these runs are not in accordance with the present and are included for purposes of comparison.

The dispersant was C6 in an amount of 1%, except for run 76 g (1% before M1 plus another 1% after M1), run 76i (more, 4.0%), and runs 76 j-k in which 1% N2 dispersant was used in place of C6.

    __________________________________________________________________________         COMPO-                                                                         NENTS: &               STRENGTH                                                                              SETTLE-                                          MIXING        NaOH                                                                               SET- S: kg/cm.sup.2                                                                        MENT                                         RUN ORDER CM  WC  %   hours                                                                               H: hours                                                                              vol. %                                       __________________________________________________________________________     76a WDMA  M1  2:1 5   12   S: >4.5                                                                               60                                                                      H: 22                                               76b WDMA (1)                                                                             M1  2:1 5   12   S: >4.5                                                                               50                                                                      H: 22                                               76c WDMA (2)                                                                             M1  2:1 5   22   S: >4.5                                                                               40                                                                      H: 180                                              76d WDMA (3)                                                                             M1  2:1 5   12   S: >4.5                                                                               15                                                                      H: 76                                               76e WDMA  M1  2:1 7.5 5    S: >4.5                                                                               30                                                                      H: 9                                                76f WDMA  M1  2:1 10  4    S: >4.5                                                                               30                                                                      H: 13                                               76g WDMA (4)                                                                             M1  0.5:1                                                                              5   0.33 S: >4.5                                                                                0                                                                 (20 Min)                                                                            H: 2.5                                              76h WDAM  M1  2:1 5   7    S: >4.5                                                                               40                                                                      H: 17                                               76i WDMA  M1  2:1 5   7    S: 4.5 50                                                                      H: 27                                               76j WDM   M3W 2:1 0   8    S: 4.5 20                                                                      H: 27                                               76k WDM   M3WO                                                                               2:1 0   8    S: 4.5  0                                                                      H: 28                                               __________________________________________________________________________      (1) 1% LiOH: accelerator was added after M1.                                   (2) 0.68% NaTF (68 wt % sodium tetraformate in water) was added after M1.      (3) 1% NaF accelerator was added after M1.                                     (4) An additional 1% of C6 dispersant added after M1.                    

COMMENTS

Runs 76 b-d: NaF gave significantly lower % settlement but long hardening time. LiOH and NaTF did not significantly lower % settlement and NaTF resulted in long hardening time.

Runs 76 e-f: 7.5 and 10% NaOH gave fast set and hardening time but higher than expected % settlement.

Run 76 g: 0.5/1 WC ratio gave a pasty mix when 5% NaOH was added. An additional 1% of C6 was added with slight viscosity reduction. This represents the practical low WC ratio for M1 with the current dispersant system.

Runs 76h: Addition of the NaOH accelerator before M1 showed better results than run 76a, the two runs being the same except for the changed sequence of mixing. However the better results in run 76h are believed to be accidental and not representative of field conditions because NaOH added to water and dispersant did not remain together for any length of time before addition of slag. The M1 was immediately added, apparently preventing any harmful reaction between NaOH and the dispersant. Under actual conditions of use in the field, NaOH added to the dispersant solution would remain there for a considerable time before addition of slag. Therefore this experiment was redesigned to provide an interval during which the water/dispersant/NaOH mixture remains standing before addition of M1. The redesigned test is reported in the following Example 6, runs 77 a-c.

Run 76i: Increase in dispersant C6 to 4% increased set and hardening time but decreased settlement compared to run 76a. C6 has previously been optimized at 1% of M1.

Runs 76 j-k: M3W and M3WO microfine portlands gave very low settlement but longer set and hardening times. Zero versus 20% settlement of M3WO and M3W showed the superior suspension properties of M3WO.

EXAMPLE 6

The effect of NaOH sequence of addition was tested in runs 77 d-e at different standing times. Runs 77 d-e test mixtures of M1 with M3 portland. The effects of lower temperatures (of the order of 10° C.) on compositions with varying NaOH accelerator concentrations were studied in runs 77 f-k.

Preparation of the composition and storage during observation of grout properties was done at ambient temperatures (normally room temperature) in runs 77 a-e and 77 l. In runs 77 f-k the compositions were prepared at temperatures below room temperature (averaging 10° C.), and storage during observation of grout properties was at 10° C.

In each of runs 77 a-l the dispersant was C6 in an amount of 1%.

    __________________________________________________________________________         COMPO-                                                                         NENTS &               STRENGTH                                                                              SETTLE-                                           MIXING        NaOH                                                                               SET-                                                                               S: kg/cm.sup.2                                                                        MENT                                          RUN ORDER CM  WC  %   hours                                                                              H: hours                                                                              vol. %                                        __________________________________________________________________________     77a WDMA  M1  2:1 5    4  S: >4.5                                                                               45                                                                      H: 13                                                77b WDAM (1)                                                                             M1  2:1 5    6  S: >4.5                                                                               50                                                                      H: 19                                                77c WDAM (2)                                                                             M1  2:1 5    6  S: >4.5                                                                               55                                                                      H: 19                                                77d WDM   M1 &                                                                               2:1 0    4  S: >4.5                                                                               30                                                      M3W             H: 120                                                         1:1                                                                  77e WDM   M1 &                                                                               2:1 0    4  S: -- (4)                                                                             20                                                      M3WO            H: --                                                          1:1                                                                  77f WDM   M1  2:1 0    6 (3)                                                                             S: >4.5                                                                               70                                                                      H: 21                                                77g WDMA  M1  2:1 2    6 (3)                                                                             S: > 4.5                                                                              65                                                                      H: 21                                                77h WDMA  M1  2:1 4    6 (3)                                                                             S: >4.5                                                                               65                                                                      H: 24                                                77i WDMA  M1  2:1 6   14  S: >4.5                                                                               55                                                                      H: 24                                                77j WDMA  M1  2:1 8    5  S: >4.5                                                                        H: 24  50                                            77k WDMA  M1  2:1 10   5  S: >4.5                                                                               30                                                                      H: 19                                                771 WDM   M5  2:1 0    3  S: >4.5                                                                               25                                                                      H: 120                                               __________________________________________________________________________      (1) NaOH: was added to water and dispersant solution, and remained             standing for 15 minutes before M1 was added.                                   (2) NaOH: was added to water and dispersant solution, and remained             standing for 30 minutes before M1 was added.                                   (3) Only a part (at the bottom) of the CM set.                                 (4) No observation (test sample lost).                                   

COMMENTS

Runs 77 a-c: Sequence of addition change with NaOH and C6 dispersant in contact for 15 minutes (77b) and 30 minutes (77c) before M1 added showed all properties of the grout decreased compared with 77a in which NaOH was added after M1. This unexpected phenomenon is believed to be very significant.

Runs 77 d-e: 50% M3W and M3WO with M1 gave satisfactory % settlement and set time but long hardening time. This is a continuing problem with the portland/slag system including M5 portland/slag (see run 77 l).

Runs 77 f-k: Two percent increments of NaOH on M1 were tested at 10° C. to confirm that the alkali activated slag reaction continues at low temperature. Although the set and hardening times were extended, the reaction did take place with best results at 10% NaOH in 77k.

EXAMPLE 7

A number of optional accelerators, or promoters of slag activation, were tested for use in combination with NaOH.

    __________________________________________________________________________         COMPO-                                                                         NENTS: &             STRENGTH                                                                              SETTLE-                                            MIXING       NaOH                                                                               SET-                                                                               S: kg/cm.sup.2                                                                        MENT                                           RUN ORDER CM WC  %   hours                                                                              H: hours                                                                              vol. %                                         __________________________________________________________________________     78a WDMA  M1 2:1 5   8   S: >4.5                                                                               50                                                                      H: 15                                                 78b WDMA (1)                                                                             M1 2:1 4   4   S: >4.5                                                                               30                                                                      H: 14                                                 78c WDMA (2)                                                                             M1 2:1 3   2   S: >4.5                                                                               20                                                                      H: 14                                                 78d WDMA (3)                                                                             M1 2:1 5   10  S: >4.5                                                                               30                                                                      H: 30                                                 78e WDMA (4)                                                                             M1 2:1 5   10  S: >4.5                                                                               40                                                                      H: 30                                                 78f WDMA (5)                                                                             M1 2:1 5   1.5 S: >4.5                                                                               10                                                                      H: 31                                                 78g WDMA (6)                                                                             M1 2:1 5   3.5 S: >4.5                                                                               20                                                                      H: 31                                                 78h WDMA (7)                                                                             M1 2:1 5   8   S: >4.5                                                                               45                                                                      H: 19                                                 78i WDMA (8)                                                                             M1 2.2:1                                                                              5.5 9   S: soft                                                                               55                                                                      H: 42                                                 78j WDMA (9)                                                                             M1 2.2:1                                                                              5.5 9   S: soft                                                                               50                                                                      H: 42                                                 __________________________________________________________________________

Added accelerators or slag activation promoters (all percentages based on weight of M1 slag):

(1) 1% Na₂ CO₃

(2) 2% Na₂ CO₃

(3) 0.4% NaF

(4) 0.8% NaF

(5) 1.0% LiS (lithium sodium polysilicate)

(6) 1.0% Li6 (lithium polysilicate)

(7) 1.0% 4130 (acrylic acid copolymer)

(8) 11.1% CaO added after NaOH

(9) 11.1% CaOH₂ added after NaOH

COMMENTS

Runs 78 b-c: Substitution of Na₂ CO₃ for part of the NaOH gave considerable improvement in set time, hardening time and % Settlement.

Runs 78 d-e: 0.4% and 0.8% NaF gave a long set time and did not harden in 14 hours.

Runs 78 f-g: Use of lithium sodium polysilicate or lithium polysilicate appears to be desirable since they gave a fast set time, medium strength and low settlement.

Runs 78 i-j: 5% CaO and Ca(OH)₂ replacement of M1 gave high settlement and remains soft after 13 hours.

In the following examples, a gray color indicates that the cement is not fully hard, a blue color shows that it is fully hard, and numerical values for compressive strength are expressed in kg/cm².

EXAMPLE 8

Experiment 60 was performed to determine set time, initial hardening time, compressive strength, clear and hard settlement for M5 MICROFINE cement and Type III Portland at 20°, 40°, 60° and 90° C.

    ______________________________________                                                           60A     60B                                                  Formulation       grams   grams                                                ______________________________________                                         Water             100     100                                                  N2                 1       1                                                   M5                100     --                                                   Type III Portland --      100                                                  ______________________________________                                         Run 60A: M5 MICROFINE Cement                                                   Viscosity at 0 hr: 15 cps (10 rpm, UL Adapter Brookfield);                     at 1 hr: 100 + cps                                                             at 20° C. Hours:                                                                    0     1     2    3   4   5    7    8   20                          % Clear Settlement                                                                         0     0     5   10  10  15   20   20   20                          % Hard Settlement 0     0    0   0   0    0    0    0                          Set Time    f.sup.(1)                                                                            f     f   f   f   f    f    f    set                         IHTS.sup.(3)                                                                               s.sup.(2)                                                                            s     s   s   s   s    s    s    2                           at 40° C. Hours:                                                                    0     1      2   3   4   5    7    8                               % Clear Settlement                                                                         0     5     10  15  15  15   15   15                               % Hard Settlement                                                                          0     0      0   0                                                 Set Time    f     f     f   f   set                                            IHTS        s     s     s   s   s   4    <4.5                                  at 60° C. Hours:                                                                    0      1     2   3   4   5    7    8                               % Clear Settlement                                                                         0     10    10  10  10  10   10   10                               % Hard Settlement                                                                          0      0     0                                                     Set Time    f     f     f   set                                                IHTS        s     s     s   s   s   0.25 b.sup.(b)                                                                           >4.5                             at 90° C. Hours:                                                                    0      1     2   3   4  5    7    8                                % Clear Settlement                                                                         0     10    10  10  10  5    5    0                                % Hard Settlement                                                                          0                                                                  Set Time    f     f     set                                                    IHTS              s     s   s   s   0.1  b                                     60B: Type III Portland (Whitehall, LaFarge)                                    Viscosity at 0 hr: 10 cps (10 rpm, UL Adapter Brookfield);                     at 1 hr: 70 cps                                                                at 20° C. Hours:                                                                    0      1     2   3   4   5    7    8                               % Clear Settlement                                                                         10    10    20  20  20  20   20   20                               % Hard Settlement                                                                          0     80    80  80                                                 Set Time    f     f     f   f   set g(5)                                       IHTS              s     s    s  s   s    0.1  4.0 >4.5                         at 40° C. Hours:                                                                    0      1     2   3   4   5    7    8                               % Clear Settlement                                                                         0     20    30  30  30  30   30   30                               % Hard Settlement                                                                          0     70    80  80                                                 Set Time    f     f     f   f   set g                                          IHTS              s     s   s   s   s    0.1  >4.5                             at 60° C. Hours:                                                                    0      1     2   3   4   5    7    8                               % Clear Settlement                                                                         0     20    30  30  30  30   30   25                               % Hard Settlement                                                                          0     70    80                                                     Set Time    f     f     set g                                                  IHTS              s     s   s   s   >4.5                                       at 90° C. Hours:                                                                    0      1     2   3   4   5    7    8                               % Clear Settlement                                                                         0     30    25  20  20  20   10   10                               % Hard Settlement                                                                          0     70                                                           Set Time    f     f     set     g.sup.(5)                                      IHTS              s     s       1   >4.5                                       ______________________________________                                          .sup.(1) fluid                                                                 .sup.(2) soft                                                                  .sup.(3) initial hardening time and strength (kg/cm.sup.2)                     .sup.(4) blue                                                                  .sup.(5) gray                                                            

EXAMPLE 9

Experiment 61 was performed to determine viscosity, clear settlement, set time, initial hardening time and compressive strength for M3 portland and M1 slag at 20°, 40°, 60° and 90° C.

    ______________________________________                                                          61A     61B                                                   Formulation      grams   grams                                                 ______________________________________                                         Water            100     100                                                   N2                1       1                                                    M3               100     25                                                    M1               --      75                                                    ______________________________________                                         61A: M3 MICROFINE cement                                                       Viscosity at 0 hr: 100 cps (10 rpm, UL Adapter Brookfield);                    at 15 min; 100 + cps                                                           at 20° C.                                                                       0       1     2    3   4    5    6    7   8                            Hours:                                                                         % Settle-                                                                              5       5     10   10  10   5    5    0                                ment 1                                                                         Set Time                                                                               f.sup.(1)                                                                              set                                                            IHTS.sup.(3)                                                                           s.sup.(2)                                                                              s     s    s   s    s    0.1  3   >4.5                         at 40° C.                                                                       0       1     2    3   4    5    6    7   8                            Hours:                                                                         %       0       0     0    0   0    0    0    0   0                            Settlement                                                                     Set Time                                                                               f set.sup.(4)                                                          IHTS    s       s     0.5  3.5 >4.5                                            at 60° C.                                                                       0       1     2    3   4    5    6    7   8                            Hours:                                                                         %       0       0     0    0   0    0    0    0   0                            Settlement                                                                     Set Time                                                                               f set.sup.(5)                                                          IHTS    s       0.1   >4.5                                                     at 90° C.                                                                       0       1     2    3   4    5    6    7   8                            Hours:                                                                         %       0       0     0    0   0    0    0    0   0                            Settlement                                                                     Set Time                                                                               f set.sup.(6)                                                          IHTS    s       0.5   >4.5                                                     61B: 75% M1/25% M3                                                             Viscosity at 0 hr: 100 cps (10 rpm, UL Adapter, Brookfield);                   at    0       1     2   3   4    5   6   7    8   9   17                       20° C.                                                                  Hours:                                                                         % Set-                                                                               0       5     5   5   5    10  10  10   5   0                            tlement                                                                        0 Set f       f     set                                                        Time                                                                           IHTS  s       s     s   s   s    s   s   s    s   0.1 4.0                      at    0       1     2   3   4    5   6   7    8   9   17                       40° C.                                                                  Hours:                                                                         % Set-                                                                               0       5     5   5   5    5   10  10   5                                tlement                                                                        Set   f       set                                                              Time                                                                           IHTS  s       s     s   s   s    s   s   s    0.1 2   >4.5                     at    0       1     2   3   4    5   6   7    8                                60° C.                                                                   Hours:                                                                        % Set-                                                                               0       5     5   5   5    0   0   0    0                                tlement                                                                        Set   f set.sup.(4)                                                            Time                                                                           IHTS  s       s     s   s   s    0.1 2   >4.5                                  at    0       1     2   3   4    5   6   7    8                                90° C.                                                                  Hours:                                                                         % Set-                                                                               0       30    25  20  20   20  10  10   10                               tlement                                                                        Set   f set.sup.(6)                                                            Time                                                                           IHTS  s       s     s   1.0 >4.5                                               ______________________________________                                          .sup.(1) fluid                                                                 .sup.(2) soft                                                                  .sup.(3) initial hardening time and strength (kg/cm.sup.2)                     .sup.(4) 40 minutes                                                            .sup.(5) 30 minutes                                                            .sup.(6) 20 minutes                                                      

EXAMPLE 10

An experiment 62 was performed which demonstrates a low density slurry and high compressive strength of the cement for 1:1 water cement ratio M5 (61A) compared with Type III portland (62A) as follows:

    ______________________________________                                                          62A      62B                                                  Formulation      (grams)  (grams)                                              ______________________________________                                         Water            100      100                                                  NS-200 Dispersant                                                                                1        1                                                   M5               100      --                                                   Type III Portland                                                                               --       100                                                                   201      201                                                  Density M5 Slurry                                                              Slurry         266 grams                                                       Tare           119                                                                            147 gm/100 ml × 8.34 = 12.3 lbs/gal                       Density Type III Portland                                                      Slurry         271 grams                                                       Tare           119                                                                            152 gm/100 ml × 8.34 = 12.7 lbs/gal                       ______________________________________                                    

Compressive strength of 1:1 WC M5 is 4500 psi at 20° C. compared with 2300 psi for other light weight blends at 27° C. This indicates that M5 MICROFINE cement has inherent properties for oi-well cementing when the combination of light weight slurry and high compressive strength is required.

EXAMPLE 11

In Experiment 63, the properties determined were viscosity, set time, initial hardening time and strength of M5 at 1:1, 0.9:1, 0.8:1, 0.7:1 and 0.5:1 water cement ratios at 20°, 60°, 70° and 80° C.

    ______________________________________                                                    63A      63B    63C    63D   63E                                    Formulation                                                                               (g)      (g)    (g)    (g)   (g)                                    ______________________________________                                         Water      100       90     80     70    50                                    N2          1        0      1       2*   2                                     MC-500     100      100    100    100   100                                    WC Ratio   1:1      0.9:1  0.8:1  0.7:1 0.5:1                                  ______________________________________                                                  Visc     Visc                                                         Viscosity                                                                               (20° C.)                                                                         (60° C.)                                              Minutes  (cps)    (cps)    Comments                                            ______________________________________                                         63A    0     5                                                                        5     10                                                                       7                                                                              10             100                                                      63B    0     6                                                                        5     8                                                                        10             15                                                              15             40                                                              20             100                                                      63C    0     11                                                                       5              25                                                              10             65                                                              12             100                                                      63D    0              100    1% N2 (based on Cement),                                 5              20     Additional 1% M2 added.                                  6               3     20° C. Heated 80° C. outside               8               2     water Measured 60° C. inside               viscometer                                                                            10              3     1% N2 (based on Cement),                                 20              5     Additional 1% N2 added,                                  25              5     20° C. Heated 80° C. outside                                     water Measured 60° C. inside               63E    0              100    2% N2 added, 20° C.                               1              45     Heated 85° C. outside                             2              10     water Measured 70° C. inside               viscometer                                                                            5              12     2% N2 added, 20° C.                               7              15     Heated 85° C. outside                                                   water Measured 60° C. inside               viscometer                                                                            10             20     2% N2 added, 20° C.                               15             25     Heated 85° C. outside                             20             25     water Measured 60° C. inside                      25              3                                                       ______________________________________                                         SET & INITIAL HARDENING TIME AND COMPRESSIVE                                   STRENGTH (kg/cm.sup.2)                                                             Hours                                                                          0       1     2    3   8    10  11   12  20   44   88                      20°  C.                                                                              80° C.                                                                             20° C.                                          A.  f.sup.(1)                                                                              f     set  s.sup.(2)                                                                          s    s   0.1.sup.(3)                                                                         0.5 2.0  >4.5 b.sup.(4)               B.  f       f     set  s   s    s   s    0.1 0.1  >4.5 b                       C.  f       f     set  s   s    s   s    0.1 0.5  >4.5 b                       D.  f       f     f    set s    s   0.1  0.5 1.0  2.0  3.0                     E.  f       f     f    set s    0.5 1.5  3.5 >4.5 g.sup.(5)                    ______________________________________                                          *1 g initially, and subsequent additional 1 g                                  .sup.(1) f = fluid                                                             .sup.(2) s = soft                                                              .sup.(3) kg/cm.sup.2                                                           .sup.(4) b = blue                                                              .sup.(5) g = gray                                                         

I claim:
 1. A method of grouting porous gas--and petroleum--bearing formations, which comprises injecting into said formation a composition comprising:(a) water (b) particulate slag, having a specific surface area greater than about 9,500 cm² /g, with less than 3 wt. percent of the particles of said slag being larger than 7.8 micrometers in diameter; the proportions of water and slag being within a water to slag weight ratio range of between 0.5:1 and 10:1; (c) at least one dispersant in an amount effective to disperse the particles of said particulate slag; and (d) an accelerator in an amount effective to provide hydraulic reactivity to said slag.
 2. A method according to claim 1, wherein less than 2 wt. percent of the particles of said slag are larger than 10 micrometers in diameter.
 3. A method according to claim 2, which comprises injecting said composition into a wellbore.
 4. A method according to claim 3, which comprises injecting said composition for primary or remedial cementing of said wellbore.
 5. A method according to claim 2, wherein the particulate slag additionally has mixed with it particulate portland cement having a particle size wherein less than 2 wt. percent of the particles of said portland cement are larger than 10 micrometers in diameter, the slag being at least 40 percent by weight of the total of portland cement and slag.
 6. A method according to claim 5, wherein the portland cement activates the hydration of the slag and partly or fully replaces said accelerator (d).
 7. A method according to claim 6, wherein the portland cement fully replaces said accelerator (d) and the particulate portland cement and particulate slag are co-ground in a proportion by weight of about 25 percent portland cement and about 75 percent particulate slag.
 8. A method according to claim 7, wherein said dispersant is up to 2 percent of a naphthalene sulfonate formaldehyde condensate by total weight of the slag and portland cement to decrease viscosity and retard set time.
 9. A method according to claim 7, wherein additionally silica flour is added in a proportion wherein the silica flour is not more than 50% of the total weight of silica flour, particulate slag and portland cement.
 10. A method according to claim 7, wherein a retarder is added in an amount effective to obtain desired longer set and hardening times for grouting under conditions of increased formation temperatures.
 11. A method according to claim 6, wherein the portland cement fully replaces said accelerator (d) and the particulate slag and the portland cement are separately ground and then mixed with the particulate slag amounting to at least 50 percent by weight of the total of portland cement and slag.
 12. A method according to claim 11, wherein the particulate slag amounts to about 75 percent and the portland cement amounts to about 25 percent by weight of the total of slag and portland cement.
 13. A method according to claim 11, wherein the proportion of slag is increased to obtain desired longer set and hardening times for grouting under conditions of increased formation temperatures.
 14. A method according to claim 11, which comprises, prior to said mixing, grinding particulate portland cement having a particle size wherein less than 10 wt. percent of the particles are larger than 10 micrometers in diameter to a particle size wherein less than 2 wt. percent of the particles are larger than 10 micrometers in diameter, in a tower mill at or near the location of said formation to be grouted.
 15. A method according to claim 13, which comprises, prior to said mixing, grinding particulate portland cement having a particle size wherein less than 10 wt. percent of the particles are larger than 10 micrometers in diameter to a particle size wherein less than 2 wt. percent of the particles are larger than 10 micrometers in diameter, in a tower mill at or near the location of said formation to be grouted.
 16. A method according to claim 12, which comprises, prior to said mixing, grinding particulate portland cement having a particle size wherein less than 10 wt. percent of the particles are larger than 10 micrometers in diameter to a particle size wherein less than 2 wt. percent of the particles are larger than 10 micrometers in diameter, in a tower mill at or near the location of said formation to be grouted.
 17. A method according to claim 7, wherein particulate slag and particulate portland cement are co-ground to a particle size wherein less than 2 wt. percent of the particles are larger than 10 micrometers in diameter in a tower mill at or near the location of said formation to be grouted.
 18. A grouting composition comprising:(a) water; (b) a particulate slag comprising a microfine slag having a specific surface area greater than about 9,500 cm² /g, with less than 3wt. percent of the particles of said slag being larger than 7.8 micrometers in diameter; the proportions of water and slag being within a water to slag weight ratio of between 0.5:1 and 1:1; (c) at least one dispersant in an amount effective to disperse the particles of said particulate slag; and (d) an accelerator in an amount to provide hydraulic reactivity to the slag.
 19. A composition according to claim 18, wherein the slag has a specific surface area greater than about 13,000 cm² /g with substantially no particles of the slag being over 7.8 micrometers in diameter.
 20. A composition according to claim 18, wherein the slag component additionally has mixed with it a cement having a specific surface area greater than about 11,000 cm² /g with less than about 7 weight percent of particles of the cement being larger than 7.8 micrometers in diameter, the slag being at least 40% of the total cementitious material by weight.
 21. A composition according to claim 20, wherein the slag has a specific surface area of at least about 14,000 cm² /g, the mixture of slag and cement having a specific surface area of at least about 12,000 cm² /g.
 22. A grouting composition comprising:(a) water; (b) a particulate slag comprising a microfine slag having a specific surface area greater than about 9,500 cm₂ /g, with less than 3 wt. percent of the particles of said slag being larger than 7.8 micrometers in diameter; the proportions of water and slag being within a water to slag weight ratio of between 0.5:1 and 10:1; (c) at least one dispersant in an amount effective to disperse the particles of said particulate slag; and (d) an accelerator in an amount effective to provide hydraulic reactivity to said slag; said composition having been prepared by mixing in sequence (a) with (c) to form a first mixture, then adding (b) to form a second mixture, then adding (d) to said second mixture, and subjecting the resulting composition to strong agitation.
 23. A composition according to claim 22, wherein the slag has specific surface area greater than about 13,000 cm² /g with substantially no particles of the slag being over 7.8 micrometers in diameter.
 24. A composition according to claim 22, wherein the slag component additionally has mixed with it a cement having a specific surface area greater than about 11,000 cm² /g with less than about 7 weight percent of particles of the cement being larger than 7.8 micrometers in diameter, the slag being at least 40% of the total cementitious material by weight.
 25. A method acording to claim 1, wherein said water to slag weight ratio is in the range between 0.5:1 and 1.5:1.
 26. A method of grouting porous gas--and petroleum--bearing formations, which comprises injecting into said formation a composition comprising:(a) water (b) particulate slag, having a specific surface area greater than about 9,500 cm² /g, with less than 3 wt. percent of the particles of said slag being larger than 7.8 micrometers in diameter; the proportions of water and slag being within a water to slag weight ratio range of between 0.3:1 and 10:1; (c) at least one dispersant in an amount effective to disperse the particles of said particulate slag; and (d) an accelerator in an amount effective to provide hydraulic reactivity to said slag.
 27. A method according to claim 26 wherein the water to slag weight ratio is in the range between 0.4:1 and 1.5:1. 